NantilusANTIMONIATES ET TITANOANTIMONIATES A STRUCTURE "TUNNELS ENTRECROISES" : LE CONDUCTEUR PROTONIQUE H::(2)SB::(4)O::(11)(H::(2)O)::(3)
SYNTHESE ET ETUDE STRUCTURALE DES PHASES K::(2)SB::(4)O::(11) (K**(1)) ET K::(3)SB::(5)O::(14)(K**(2)). ETUDE DES PYROCHLORES K::(0,51)SB::(0,67)**(III)SB::(2)**(V)O::(6,26) ET TL::(0,51)SB::(0,72)**(III)SB::(2)**(V)O::(6,32). PROPRIETES D'ECHANGE DES PHASES K**(1) ET K**(2): CONDUCTIVITE ELECT...
Enregistré dans:
| Auteur principal : | |
|---|---|
| Format : | Thèse ou mémoire |
| Langue : | français |
| Titre complet : | ANTIMONIATES ET TITANOANTIMONIATES A STRUCTURE "TUNNELS ENTRECROISES" : LE CONDUCTEUR PROTONIQUE H::(2)SB::(4)O::(11)(H::(2)O)::(3) / YVES PIFFARD |
| Publié : |
[S.l.] :
[s.n.]
, 1980 |
| Description matérielle : | 110 P. |
| Note de thèse : | DOCTORAT D'ETAT : PHYSIQUE : Nantes : 1980 |
| Sujets : |
| LEADER | 02679cam a22003851i 4500 | ||
|---|---|---|---|
| 001 | PPN042369916 | ||
| 005 | 20170501015100.0 | ||
| 035 | |a 072537205 | ||
| 035 | |a thS-00024423 | ||
| 035 | |a DYNIX_BUNAN_215302 | ||
| 100 | |a 19990313d1980 |||||frey0103 ba | ||
| 101 | 0 | |a fre |d fre | |
| 102 | |a FR | ||
| 105 | |a y m ||||| | ||
| 200 | 1 | |a ANTIMONIATES ET TITANOANTIMONIATES A STRUCTURE "TUNNELS ENTRECROISES" |e LE CONDUCTEUR PROTONIQUE H::(2)SB::(4)O::(11)(H::(2)O)::(3) |f YVES PIFFARD | |
| 210 | |a [S.l.] |c [s.n.] |d 1980 | ||
| 215 | |a 110 P. |d 30 cm | ||
| 320 | |a 77 REF | ||
| 328 | 0 | |b DOCTORAT D'ETAT |c PHYSIQUE |e Nantes |d 1980 | |
| 330 | |a SYNTHESE ET ETUDE STRUCTURALE DES PHASES K::(2)SB::(4)O::(11) (K**(1)) ET K::(3)SB::(5)O::(14)(K**(2)). ETUDE DES PYROCHLORES K::(0,51)SB::(0,67)**(III)SB::(2)**(V)O::(6,26) ET TL::(0,51)SB::(0,72)**(III)SB::(2)**(V)O::(6,32). PROPRIETES D'ECHANGE DES PHASES K**(1) ET K**(2): CONDUCTIVITE ELECTRIQUE. ETUDE PAR RMN A 1,5 ET 4,2 K DES PHASES H::(2)SB::(4)O::(11)(H::(2)O)::(3,1) ET H::(2)SB::(4)O::(11)(H::(2)O)::(2,15). ETUDE DE K::(2+X)SB::(4-X)TI::(X)O::(11) PAR MICROSCOPIE ET DIFFRACTION ELECTRONIQUE, ASPECT ELECTROSTATIQUE DE LA REPARTITION DU TITANE ET DU POTASSIUM DANS LA STRUCTURE DU COMPOSE OBTENU POUR X=0,38. STRUCTURE CRISTALLINE DE KTI::(3)SBO::(9) | ||
| 610 | 1 | |a PHYSIQUE : ETAT CONDENSE : PROPRIETES MECANIQUES ET THERMIQUES | |
| 610 | 2 | |a RESONANCE MAGNETIQUE NUCLEAIRE/PROFIL RAIE SPECTRALE/TRES BASSE TEMPERATURE/CONDUCTIVITE ELECTRIQUE/CONDUCTIVITE IONIQUE/CONDUCTEUR SUPERIONIQUE/TEMPERATURE/BASSE TEMPERATURE/CONDUCTIVITE PROTONIQUE/HYDRATATION/STRUCTURE CRISTALLINE/ANALYSE DIFFRACTION RX/COMPOSE MINERAL/METAL ALCALIN COMPOSE/PYROCHLORES/POTASSIUM ANTIMONIATE/POTASSIUM ANTIMONIATE TITANATE/ANTIMOINE III ANTIMOINE V POTASSIUM OXYDE MIXTE/METAL TRANSITION COMPOSE | |
| 610 | 2 | |a NUCLEAR MAGNETIC RESONANCE/SPECTRAL LINE PROFILE/VERY LOW TEMPERATURE/ELECTRICAL CONDUCTIVITY/TEMPERATURE/LOW TEMPERATURE/HYDRATION/CRYSTALLINE STRUCTURE/INORGANIC COMPOUND/ALKALI METAL COMPOUND/POTASSIUM ANTIMONATE/POTASSIUM ANTIMONATE TITANATE/ANTIMONY III ANTIMONY V POTASSIUM OXIDE MIXED | |
| 686 | |a 001.B.60_001.B.60 |2 tlt | ||
| 700 | 1 | |a Piffard |b Yves |4 070 | |
| 801 | 3 | |a FR |b Abes |c 20050322 |g AFNOR | |
| 801 | 3 | |a FR |b Abes |c 20050322 |g AFNOR | |
| 915 | |5 441092104:179901788 |a 1160625111 |b 1160625111 | ||
| 915 | |5 441092104:179901796 |a 1160625128 |b 1160625128 | ||
| 919 | |5 441092104:179901788 |a 1160625111 | ||
| 919 | |5 441092104:179901796 |a 1160625128 | ||
| 930 | |5 441092104:179901788 |b 441092104 |a 80 NANT Piffard 2ex |j u | ||
| 930 | |5 441092104:179901796 |b 441092104 |a 80 NANT Piffard 3ex |j u | ||
| 979 | |a SCI | ||
| 998 | |a 172256 | ||